GUR® 4150
超高分子量聚乙烯
Celanese Corporation
产品说明
GUR 4150 UHMW-PE is a linear polyolefin resin in powder form with a molecular weight of
approximately 9.2 MM g/mol calculated using Margolies' equation. The extremely high molecular
weight of this resin yields several unique properties including superior abrasion resistance and
impact strength. This and GUR 4152 resins have the best abrasion resistance of all standard grades.
Outstanding properties include a low coefficient of friction that results in self-lubricating, non-stick
surfaces after processing. The resin is normally processed by compression molding or ram extrusion.
基本信息
UL 黄卡E223637-542521
特性
超高分子量低摩擦系数抗撞击性,良好良好耐磨损性
自润滑
RoHS 合规性联系制造商
形式粉状
加工方法挤出压缩模塑
物理性能额定值单位制测试方法
比重
-- 0.928 g/cm³ ASTM D792
-- 0.930 g/cm³ ISO 1183
熔流率(熔体流动速率) (190°C/21.6 kg) < 0.10 g/10 min ASTM D1238, ISO 1133
吸水率 ISO 62
饱和, 23°C < 0.010 % ISO 62
平衡, 23°C, 50% RH < 0.010 % ISO 62
粘数 3850 cm³/g ISO 307
Elongational Stress F - 150/10 0.510 MPa ISO 1152-2
固有粘度 32 dl/g ISO 1628-3
机械性能额定值单位制测试方法
Wear by Sandslurry Method 1 80.0 内部方法
磨损量 80.0 内部方法
冲击性能额定值单位制测试方法
Charpy Impact Strength 2 130 kJ/m² ISO 1152-2
硬度额定值单位制测试方法
肖氏硬度
邵氏 D 61 ASTM D2240
邵氏 D, 15 秒 61 ISO 868
球压硬度 3 35.0 MPa ISO 2039-1
机械性能额定值单位制测试方法
拉伸模量
23°C 703 MPa ASTM D638
-- 680 MPa ISO 527-2/1A/1
抗张强度
屈服, 23°C 21.4 MPa ASTM D638
屈服 17.0 MPa ISO 527-2/1A/50
伸长率
屈服, 23°C < 20 % ASTM D638
屈服 20 % ISO 527-2/1A/50
断裂, 23°C > 350 % ASTM D638
标称拉伸断裂应变 > 50 % ISO 527-2/1A/50
拉伸蠕变模量 ISO 899-1
1 hr 430 MPa ISO 899-1
1000 hr 220 MPa ISO 899-1
摩擦系数 (与钢 - 动态) 0.10 内部方法