备注说明: 特性:玻纤增强30%
1015GC6 物性表
基本性能额定值单位测试方法
吸水率 | 1.3 | % | ASTM D-570 |
成型收缩率 | 0.4 | % | UBEmethod |
吸水率 | 7.4 | % | ASTM D-570 |
成型收缩率 | 0.7 | % | UBEmethod |
物理性能额定值单位测试方法
比重 | 1.28 | ASTM D-792 |
机械性能额定值单位测试方法
屈服下的伸张强度 (23°) | 1320 | kgf/cm | ASTM D-638 |
挤剪强度 (23°) | 710 | kgf/cm | ASTM D-732 |
屈服下的伸张强度 (23°) | 750 | kgf/cm | ASTM D-638 |
弯曲强度 (23°) | 900 | kgf/cm | ASTM D-790 |
硬度(洛氏.布氏) (23°) | 95 | ASTM D-785 | |
1%变形下的压缩强度 (23°) | 140 | kgf/cm | ASTM D-695 |
弯曲弹性率 | ASTM D-790 | ||
(-30°) | 83000 | kgf/cm | |
(-30°) | 90000 | kgf/cm | |
挤剪强度 (23°) | 530 | kgf/cm | ASTM D-732 |
断裂下的延伸率 | 5 | % | ASTM D-638 |
屈服下的伸张强度 (-30°) | 1850 | kgf/cm | ASTM D-638 |
Taber磨耗率 | 13 | mg | ASTM D-1044 |
弯曲弹性率 (23°) | 61000 | kgf/cm | ASTM D-790 |
抗冲击强度 (23°) | 10 | kgf.cm/cm | ASTM D-256 |
硬度(洛氏.布氏) (23°) | 120 | ASTM D-785 | |
断裂下的延伸率 (23°) | 5 | % | ASTM D-638 |
弯曲强度 (23°) | 1850 | kgf/cm | ASTM D-790 |
抗冲击强度 (23°) | 8.0 | kgf.cm/cm | ASTM D-256 |
弯曲弹性率 (80°) | 23000 | kgf/cm | ASTM D-790 |
硬度(洛氏.布氏) (23°) | 100 | ASTM D-785 | |
弯曲弹性率 (23°) | 31000 | kgf/cm | ASTM D-790 |
1%变形下的压缩强度 (23°) | 250 | kgf/cm | ASTM D-695 |
屈服下的伸张强度 (80°) | 650 | kgf/cm | ASTM D-638 |
弯曲弹性率 (80°) | 37500 | kgf/cm | ASTM D-790 |
电气性能额定值单位测试方法
介电损耗 | ASTM D-150 | ||
(60HZ) | 0.11 | ||
(10HZ) | 0.02 | ||
介电常数 (10HZ) | 3.6 | ASTM D-150 | |
体积电阻率 | 10 | Ω.cm | ASTM D-257 |
介电常数 (60HZ) | 4.0 | ASTM D-150 | |
IEC电路 | 550 | V | UL746 |
介电常数 (10HZ) | 4.6 | ASTM D-150 | |
抗电弧强度 | 121 | S | ASTM D-495 |
介电常数 (10HZ) | 3.9 | ASTM D-150 | |
介电损耗 | ASTM D-150 | ||
(10HZ) | 0.10 | ||
(10HZ) | 0.01 | ||
介电常数 | ASTM D-150 | ||
(60HZ) | 9.0 | ||
(10HZ) | 8.0 | ||
介电损耗 | ASTM D-150 | ||
(60HZ) | 0.01 | ||
(10HZ) | 0.09 | ||
体积电阻率 | 10 | Ω.cm | ASTM D-257 |
热性能额定值单位测试方法
热变形温度 (4.6kgf/cm) | 215 | °C | ASTM D-648 |
熔点 (DSC) | 215-225 | °C | |
燃烧率 | HB | UL94 | |
线性热膨胀系数 | 3.5 | X的10-5cm/cm/°C | ASTM D-696 |
热变形温度 (18.6kgf/cm) | 200 | °C | ASTM D-648 |
40
kg.cm/cm
IZOD冲击强度 23℃,无缺口1/8 --- 无断裂 -
kg.cm/cm
洛氏硬度 23℃ ASTM D-785 119 90
---
洛氏硬度 23℃ ASTM D-785 83 -
---
抗拉屈服强度 -40 ASTM D-638 1230 1150
Kg/cm2
抗拉屈服强度 23℃ ASTM D-638 820 420
Kg/cm2
抗拉屈服强度 80℃ ASTM D-638 320 220
Kg/cm2
抗拉断裂强度 23℃ ASTM D-638 20 -
Kg/cm2
断裂伸长率 23℃ ASTM D-638 180 <200
%
挠曲强度 -40℃ ASTM D-790 1500 1450
Kg/cm2
挠曲强度 23℃ ASTM D-790 1100 450
Kg/cm2
挠曲强度 80℃ ASTM D-790 500 300
Kg/cm2
挠曲模量 -40℃ ASTM D-790 40000 37000
Kg/cm2
挠曲模量 23℃ ASTM D-790 29000 10000
Kg/cm2
挠曲模量 80℃ ASTM D-790 8000 4000
Kg/cm2
压缩强度 23℃ ASTM D-695 890 -
Kg/cm2
搞剪强度 23℃ ASTM D-732 740 690
Kg/cm2
IZOD冲击强度 -40℃,无缺口1/2 --- 3.5 15
kg.cm/cm
电气性能 体积电阻率 --- ASTM D-257 1014-1015 1011-1012
Ω.cm
介电强度 1/8" ASTM D-149 20 -
KV/mm
介电常数 50HZ ASTM D-150 4.1 -
---
介电常数 106Hz ASTM D-150 3.9 -
---
介电常数 106Hz ASTM D-150 3.4 -
---
损耗因素 50Hz ASTM D-150 50Hz -
---
损耗因素 103Hz ASTM D-150 0.06 -
---
损耗因素 106Hz ASTM D-150 0.03 -
---
抗电弧性 1/8" ASTM D-150 121 -
---
IEC导电径踪指数 --- UL 746 ≤600 -
V
热 性 能 线性热膨胀系数 --- ASTM D-696 8 -
10-5cm/cm.℃
热挠曲温度 --- ASTM D-648 190 -
℃
热挠曲温度 18.6kg/cm2 ASTM D-648 190 -
℃
UL-94抗燃级 --- UL 94 V-2(1/16") -
---
熔点 --- 差示扫描测热计DSC法 225 -
℃
比热 --- --- 0.46 -
Cal/g.°C
导热系数 --- --- 0.18 -
Kcal/m.hr.°C